Research on Space Irradiation Environment Adaptability of J312L Structural Adhesive
Author:
Affiliation:

1.China Academy of Space Technology,Beijing 100094;2.China Academy of Aerospace Standardization and Product Assurance,Beijing 100071

Clc Number:

V45

Fund Project:

  • Article
  • |
  • Figures
  • |
  • Metrics
  • |
  • Reference
  • |
  • Related
  • |
  • Cited by
  • |
  • Materials
  • |
  • Comments
    Abstract:

    To investigate the influence of space irradiation on the properties of J312L structural adhesive, micromorphology, molecular structure, heat resistance, vacuum pollution and mechanical properties of J312L were analyzed by SEM, FT-IR, XPS, TGA, DSC, vacuum outgassing and mechanical test. The irradiation aging mechanism of material was investigated. The results show that the total dose irradiation has a significant effect on the thermal stability, vacuum outgassing and mechanical properties of J312L adhesive. After 1.5×109 rad(Si) γ-ray irradiation from 60Co, the tensile shear strength is 4.8 MPa, and the total vacuum mass loss (TML) is 2.36%. Compared to that of the initial, the glass transition temperature and the thermal decomposition temperature (Td 5%) are reduced by 31 ℃ and 84 ℃, respectively, indicating that the J312L adhesive is dominated by the degradation reactions within high-dose radiation.

    Reference
    Related
    Cited by
Get Citation
Share
Article Metrics
  • Abstract:
  • PDF:
  • HTML:
  • Cited by:
History
  • Received:September 05,2022
  • Revised:March 29,2023
  • Adopted:December 26,2022
  • Online: April 26,2023
  • Published: April 30,2023