基体预热温度对ZrO2 涂层结合强度的影响
作者:
作者单位:

第二炮兵青州士官学校工程系


Eeffect of Substrate Preheating Temperature onTensile Strength of Thermal Barrier Coatings
Author:
  • 摘要
  • | |
  • 访问统计
  • |
  • 参考文献 [3]
  • |
  • 相似文献 [20]
  • | | |
  • 文章评论
    摘要:

    用等离子喷涂的方法在不同温度的45#钢基体上制备ZrO2 涂层,通过涂层的结合实验、X 射线衍
    射分析了基体温度与涂层结合强度之间的关系,发现当基体预热温度为250益时涂层的结合强度最高,可达
    13. 4 MPa;当预热温度高于350益时,粘结层中的热生长氧化物明显增加,导致涂层的结合强度降低。

    Abstract:

    ZrO2 coating was developed by plasma spraying process in different substrate preheating temperature, and the tensile test and XRD were used to investigate the influence of substrate preheating temperature on tensile strength. The highest tensile strength can be obtained when the substrate preheating temperature is 250, the highest value is 13.4 MPa.When substrate preheating temperature is higher than 350, the mass of the thermally grown oxide on bond coatings increased more and the tensile strength reduced.

    参考文献
    [1] 范希梅,林洁琼,杜贤昌. 热障涂层的研究现状[J].长春工业大学学报,2003,24(1):22-23
    [2] 陈和兴,镍基合金基体热障涂层界面扩散和反应研究[D]. 中南大学,2004:45-65
    [3] 陈和兴,周克松,金展鹏. 等离子喷涂热障涂层失效机理的研究[J]. 广东有色金属学报,2002,12(2):166-169
    引证文献
引用本文

王德朋 李庆会 王旭东.基体预热温度对ZrO2 涂层结合强度的影响[J].宇航材料工艺,2010,40(3).

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 在线发布日期: 2016-11-28
文章二维码