Analysis of Hard Impurity Defect of Titanium Alloy

Author:

Affiliation:

Fund Project:

摘要

图/表

访问统计

参考文献

相似文献

引证文献

资源附件

文章评论

摘要:

采用 VAR 三次熔炼方法制备含有 YG8 刀具硬质合金杂质的铸锭,铸锭经开坯改锻制成 Φ40 mm

棒材,超声波探伤确定杂质位置。用光学显微镜和扫描电镜对杂质边缘的组织形貌及成分进行分析。研究结

果表明,硬质合金部分熔化,边界含有明显的过渡区域,过渡区含有钛合金基体元素和刀具硬质合金元素并发

生了扩散。杂质的存在会引起应力集中,容易萌生疲劳裂纹,进而影响产品的使用性能。

Abstract:

The ingot including impurity of YG8 cutter hard alloy was made by the measure of VAR. Φ40 mm

bars were made from ingot by forging and the position of impurity was located by ultrasonic detection. The appearance

of impurity was observed through optical microscope and SEM. The results show that hard alloy melts partially and the

boundary has transition area. The transition area includes elements of titanium and elements of cutter hard alloy,

where diffusion happens. The existence of impurity leads to stress focus which produces fatigue flaw easily, then influ-

ences the quality of product.

参考文献

相似文献

引证文献

引用本文

李雪飞.钛合金硬质夹杂缺陷分析[J].宇航材料工艺,2015,45(6).

复制

文章指标

点击次数:
下载次数:
HTML阅读次数:
引用次数:

历史

收稿日期:
最后修改日期:
录用日期:
在线发布日期: 2016-11-28
出版日期:

投稿方式

引用本文

分享

文章指标

历史